Nafion™ polymer, was developed by Dr. Walther Grot at DuPont in the late 1960’s by modifying Teflon™. Nafion™ polymer was the first synthetic polymer ever developed with ionic properties, and it started an entirely new class of polymers called ionomers. These ionic properties of Nafion™ polymer were created by adding sulfonic acid groups, a chemical with very strong ionic properties, into the bulk polymer matrix. Nafion™ polymer combines the physical and chemical properties of its Teflon™ base material with ionic characteristics that give the final material the following properties:

  • Like Teflon™, Nafion™ polymer is extremely resistant to chemical attack. According to DuPont, only metallic alkali metals (sodium in particular) can attack Nafion™ polymer directly under normal conditions of temperature and pressure. This means Nafion™ polymer does not release fragments or degradation products into the surrounding medium.
  • Like Teflon™, Nafion™ polymer  has relatively high working temperatures compared to many polymers. Nafion™ polymer is used in some applications at temperatures up to 190° C.
  • Unlike Teflon™, Nafion™ polymer  is highly ion-conductive. It functions as a cation exchange polymer.
  • Nafion™ polymer is a super-acid catalyst. The sulfonic acid groups attached to the Teflon™ backbone within Nafion™ polymer function as an extremely strong proton donor due to the stabilizing effect of the large polymer matrix attached to the sulfonic acid.
  • Nafion™ polymer is very selectively and highly permeable to water. The sulfonic acid groups in Nafion™ polymer have a very high water-of-hydration, so they very efficiently absorb water. Interconnections between the sulfonic acid groups lead to very rapid transfer of water through the Nafion™ polymer.


These unusual properties are exploited in the four main applications of Nafion™ polymer today.

  • Nafion™ polymer  is used to fabricate ion-exchange membranes used to produce chlorine gas and lye (sodium hydroxide) by the electrolysis of salt water.
  • Nafion™ polymer is used to selectively dry or to humidify gases. The largest segment of this application involves drying or humidifying breath for anesthesia, respiratory care, or plethysmography, but many applications exist in the laboratory and in industrial use.
  • Nafion™ polymer is used as the proton exchange membranes in polymer electrode fuel cells.
  • Nafion™ polymer is used as a super-acid catalyst in the production of fine chemicals.

Physical Appearance

Nafion™ polymer  is initially produced in a salt form with its sulfonic acid groups neutralized. In this form, Nafion™ polymer is thermoplastic (extrudable and formable using heat and pressure), but not chemically active. Once extruded into its final form (typically sheet or tubing), Nafion™ polymer is chemically activated by conversion of the salt form to the acid form. At this stage, Nafion™ is a translucent plastic that is similar in appearance to Teflon, but clearer and less opalescent.
Once activated, Nafion™ polymer  immediately begins to react with its surrounding environment. Water vapor is absorbed and exchanged with the surroundings. Reactive organic gas components within the surrounding air may undergo chemical changes when exposed to the super-acid catalytic activity of Nafion™ polymer. These organic gases may combine to form larger compounds that are liquid or solid in nature. Over time, these organic residues build up a deposit on the Nafion™ polymer. The original color of the Nafion™ polymer changes gradually from translucent to yellow, then brown, then even black.
The chemical nature of the Nafion™ polymer itself is not changed by this process. The Nafion™ polymer is not directly attacked, and the Nafion™ polymer  is not degraded. Its properties of water permeability, ion-exchange, and acid catalysis are not directly affected.
For Nafion™ polymer to transport water (dry or humidify gases), the water must be able to reach the active sites on the surface of the Nafion™ polymer. In extreme cases, deposits of organic residues can build up on the Nafion™ polymer to the point where the surface of the Nafion™ polymer is sufficiently occluded to reduce its functionality. When this occurs, the discoloration of the Nafion™ polymer is severe, black rather than merely yellow or brown. Even in these extreme cases, Nafion™ is still functional, it merely loses efficiency. Loss of a few percent of its total functionality due to partial occlusion means that a gradual decline in performance will be observed, not a catastrophic failure.
Under typical storage or operating conditions, Nafion™ polymer will turn somewhat yellow within a year and brown within three to five years. Even after turning brown, the Nafion™ polymer is still fully functional, and no loss of performance efficiency is likely to be observed.
These unwanted chemical reactions in the air surrounding Nafion™ polymer are stimulated by exposure to light and to elevated temperatures. Storage in sealed bags in the dark will extend the pristine original appearance of Nafion™ polymer.
Performance of Perma Pure’s MD, PD or ME Series gas dryers may decline over time due to buildup of residues on the inside or outside of the Nafion™ tubing within the dryer. Perma Pure recommends replacing a worn dryer assembly with a new and complete dryer assembly. Full factory OEM performance will not be restored by cleaning an element, and any unit that has been cleaned will be exempt from coverage under our manufacturer’s warranty. A brand new, factory-assembled, leak-tested, and fully functional dryer will provide reliable operation and optimal performance, and will also be backed by our warranty. Please complete our Order Form and submit it to your local Perma Pure contact to place an order for a new dryer.